岡 弘; 丹野 敬嗣; 大塚 智史; 矢野 康英; 皆藤 威二
Nuclear Materials and Energy (Internet), 16, p.230 - 237, 2018/08
被引用回数:4 パーセンタイル:38.11(Nuclear Science & Technology)In determining the nitrogen concentration specifications, nano-structure and high-temperature strength of 9Cr-ODS steel have been investigated as a function of the nitrogen content with the aim of obtaining technical knowledge that makes the specification reasonable. The hardness and tensile strength showed degradation with increasing nitrogen content. For a microstructure, the decrement of residual ferrite phase was confirmed. Since the nitrogen is an austenite stabilizer, the increment of nitrogen enhanced an alpha to transformation, resulted in the decrease of the residual ferrite phase. It is considered that the reduction of the strength is due to the decrease of the residual ferrite phase.
Nyilas, A.*; Obst, B.*; 中嶋 秀夫
Proceedings of 3rd International Conference on High Nitrogen Steels (HNS-93), p.339 - 344, 1993/00
原研が鉄鉱メーカと共同で開発した窒素強化型のステンレス鋼(Fe-25Cr-15Ni-0.35N,CSUS-JN1)の極低温における引張特性、破壊靱性及び疲労き裂進展特性についての測定結果について報告している。測定結果より、この新しく開発された材料は、極低温で1,300MPaの耐力を有し、217MPa√mの破壊靱性を有する非常に優れた材料であることが実証された。また。疲労き裂の進展特性も既存の316LN鋼よりも優れていることがわかった。